Doesn't look like you have enough heat on the main body, the blue glow barely extends past the weld in some places, the tack weld has a better heat radius. Is the body thicker than the gusset you welded?
How can I adjust my camera so it is just a bit blurry, so no welds will be visible in the pictures?You gotta be a glutton for punishment to post a picture of a weld at this point. :P I would ride with all the welds I have seen so far.Also dimes, no dimes, who gives a shit. That basically has nothing to do with the weld strength, just asthetics. I have seen cold dimes that held nothing, and absolutely smooth beeds that had great penetration.I am going to start taking pictures of the farm crap that comes to my shop....... You guys don't know what bad welds are.
I am going to start taking pictures of the farm crap that comes to my shop....... You guys don't know what bad welds are.
Adam i think that your just a hater.Of course there done with TIG no MIG can weld so clean. The HAZ(heat affected zone) is so big due to welding with TIG. If you've used it before you would realize that what you get from it.One thing all these welders have in common. Practice and consistency which comes with practice .
It might make for a bit of friendly competition.